Phase mixture single layer film with 3-dimensional spatial distribution of internal interfaces between ferromagnetic and antiferromagnetic nanoclusters was achieved through the inhomogeneous distribution of oxygen atoms within the ferromagnetic transition metal thin film layer. In the present work, enhanced exchange bias properties of phase mixture single layer film including both exchange and super-exchange couplings within the body of the single layer were investigated under various conditions. The film exhibited same exchange bias field regardless of the layer thickness, which violates the known relationship of inverse proportionality between the exchange bias field and the thickness of the magnetic layer in the conventional ferromagnet/antiferromagnet bilayers systems. Furthermore, it was found that the exchange bias could be set in any direction with respect to the film surface, removing the restriction by the magnetic shape anisotropy of the thin film structure. Low blocking temperature of the phase mixture single layer film could also be overcome with an additional neighboring antiferromagnet layer.

The effect of electric current pulses on a sub-100 nm magnetic bubble state in a symmetric Pt/Co multilayer was directly observed using a full-field transmission soft X-ray microscope (MTXM). Field-induced evolution of the magnetic stripe domains into isolated bubbles with their sizes down to 100 nm was imaged under varying external magnetic fields. Electric current pulses were then applied to the created magnetic bubbles, and it was observed that the bubbles could be either created or annihilated by the current pulse depending on the strength of applied magnetic field. The results suggest that the Joule heating plays a critical role in the formation and/or elimination of the bubbles and skyrmions. Finally, the schematic phase diagram for the creation and annihilation of bubbles is presented, suggesting an optimized scheme with the combination of magnetic field and electric current necessary to utilize skyrmions in the practical devices.

At the interface between ferromagnetic and antiferromagnetic phases, various spin configurations with a higher degrees of complexity than in the bulk states can be derived due to the diverse possible interface atomic structures, where coupling interactions among the constituting atoms can form in consistence with altered atomic configurations. The interface magnetic properties then depend on the collective behavior of such spin structures. In the present work, an extended interfacial configuration of a hypo-oxide state was prepared by establishing the gradient of oxygen concentration across the spatially diffuse interface region between ferromagnetic metallic and antiferromagnetic oxide phases at the nanometer scale. With these mixed ferromagnetic and antiferromagnetic couplings among the atoms in the interfacial hypo- or sub-oxide state, novel magnetic behavior can be induced. We report here, for the first time, a significant increase of saturation magnetization with temperature over a broad temperature range, which is against the conventional expectation for any generally known magnetic materials. And the unusual temperature dependent behavior can be understood as the combined effects of competing ferromagnetic and antiferromagnetic couplings acting on atoms in and near the interface region.

The non-trivial topology of magnetic structures such as vortices and skyrmions is considered as a key concept to explain the stability of those structures. The stability, dictated by non-trivial topology, provides great potential for device applications. Although it is a very critical scientific and technological issue, it is elusive to experimentally study the topology-dependent stability owing to the difficulties in establishing stably formed magnetic structures with different topologies. Here, we establish a platform for vortex-antivortex structures with different topological charges within Ni80Fe20 rectangular elements thick enough to stabilize a unique three-dimensional magnetic structure with non-uniform magnetization along the thickness of the elements. The detailed magnetization configurations of the three-dimensional vortex-antivortex structures and their annihilations during their field-driven motions are investigated by utilizing magnetic transmission soft x-ray microscopy and micromagnetic simulation. We demonstrate that the stability of vortex-antivortex structures significantly depends on their topologies and the topology-dependent stability is associated with their different annihilation mechanisms. We believe that this work provides in-depth insight into the stability of magnetic structures and its topology dependence.

The topological spin textures in magnetic vortices in confined magnetic elements offer a platform for understanding the fundamental physics of nanoscale spin behavior and the potential of harnessing their unique spin structures for advanced magnetic technologies. For magnetic vortices to be practical, an effective reconfigurability of the two topologies of magnetic vortices, that is, the circularity and the polarity, is an essential prerequisite. The reconfiguration issue is highly relevant to the question of whether both circularity and polarity are reliably and efficiently controllable. In this work, we report the first direct observation of simultaneous control of both circularity and polarity by the sole application of an in-plane magnetic field to arrays of asymmetrically shaped permalloy disks. Our investigation demonstrates that a high degree of reliability for control of both topologies can be achieved by tailoring the geometry of the disk arrays. We also propose a new approach to control the vortex structures by manipulating the effect of the stray field on the dynamics of vortex creation. The current study is expected to facilitate complete and effective reconfiguration of magnetic vortex structures, thereby enhancing the prospects for technological applications of magnetic vortices.

A Bloch point (BP) is a topological defect in a ferromagnet at which the local magnetization vanishes. With the difficulty of generating a stable BP in magnetic nanostructures, the intrinsic nature of a BP and its dynamic behaviour has not been verified experimentally. We report a realization of steady-state BPs embedded in deformed magnetic vortex cores in asymmetrically shaped Ni₈₀Fe₂₀ nanodisks. Time-resolved nanoscale magnetic X-ray imaging combined with micromagnetic simulation shows detailed dynamic character of BPs, revealing rigid and limited lateral movements under magnetic field pulses as well as its crucial role in vortex-core dynamics. Direct visualizations of magnetic structures disclose the unique dynamical feature of a BP as an atomic scale discrete spin texture and allude its influence on the neighbouring spin structures such as magnetic vortices.

Harmonic oscillation of spin structures is a physical phenomenon that offers great potential for applications in nanotechnologies such as nano-oscillators and bio-inspired computing. The effective tuning of oscillations over wide frequency ranges within a single ferromagnetic nanoelement is a prerequisite to realize oscillation-based nanodevices, but it has not been addressed experimentally or theoretically. Here, utilizing a vortex core structure, one of spin structures, we report a drastic change of oscillation modes over the frequency range from MHz to sub-GHz in a 100 nm-thick permalloy circular disk. Oscillation mode was found to considerably depend on the shape and dimension of the vortex core structure and various oscillation modes over a wide range of frequencies appeared with dimensional change in the vortex core structure. This work demonstrates that oscillation modes of the vortex core structure can be effectively tuned and opens a way to apply spin structures to oscillation-based technology.

Magnetic skyrmions are topologically protected spin textures with attractive properties suitable for high-density and low-power spintronic device applications. Much effort has been dedicated to understanding the dynamical behaviours of the magnetic skyrmions. However, experimental observation of the ultrafast dynamics of this chiral magnetic texture in real space, which is the hallmark of its quasiparticle nature, has so far remained elusive. Here, we report nanosecond-dynamics of a 100nm-diameter magnetic skyrmion during a current pulse application, using a time-resolved pump-probe soft X-ray imaging technique. We demonstrate that distinct dynamic excitation states of magnetic skyrmions, triggered by current-induced spin-orbit torques, can be reliably tuned by changing the magnitude of spin-orbit torques. Our findings show that the dynamics of magnetic skyrmions can be controlled by the spin-orbit torque on the nanosecond time scale, which points to exciting opportunities for ultrafast and novel skyrmionic applications in the future.