We report a "one-step" method for preparing conductive thin films with cylindrical microdomains oriented normal to the surface over large areas using the supramolecular assembly of poly(styrene-block-4-vinylpyridine) (PS₁₉-b-P4VP₅) and 5,10,15,20-tetrakis(4-hydroxyphenyl)-21H,23H-porphine (HOTPP). HOTPP interacts with the P4VP block by hydrogen bonding between the hydroxyl group of HOTPP and pyridine ring of PS₁₉-b-P4VP₅, forming cylindrical P4VP(HOTPP) domains having an average diameter of ∼17 nm in a PS matrix. Dynamic light scattering, contact angle, and in situ grazing incidence small-angle X-ray scattering measurements show a morphological transition from spherical micelles in solution to cylindrical microdomains oriented normal to the substrate surface during the drying process. From the dependence of current on voltage, an average current of ∼4.0 nA is found to pass through a single microdomain, pointing to a promising route for organic semiconductor device applications.

Locking nonequilibrium shapes of liquids into targeted architectures by interfacial jamming of nanoparticles is an emerging area in material science. 5,10,15,20-tetrakis(4-sulfonatophenyl) porphyrin (H₆ TPPS) shows three different aggregation states that present an absorption imaging platform to monitor the assembly and jamming of supramolecular polymer surfactants (SPSs) at the liquid/liquid interface. The interfacial interconversion of H₆ TPPS, specifically H₄ TPPS^2- dissolved in water, from J- to an H-aggregation was induced by strong electrostatic interactions with amine-terminated polystyrene dissolved in toluene at the water/toluene interface. This resulted in color-tunable liquids due to interfacial jamming of the SPSs formed between H₄ TPPS^2- and amine-terminated polystyrene. However, the formed SPSs cannot lock in nonequilibrium shapes of liquids. In addition, a self-wrinkling behavior was observed when amphiphilic triblock copolymers of PS-block-poly(2-vinylpyridine)-block-poly(ethylene oxide) were used to interact with H₄ TPPS^2- . Subsequently, the SPSs formed can lock in nonequilibrium shapes of liquids.

With the interfacial jamming of nanoparticles (NPs), a load-bearing network of NPs forms as the areal density of NPs increases, converting the assembly from a liquid-like into a solid-like assembly. Unlike vitrification, the lineal packing of the NPs in the network is denser, while the remaining NPs can remain in a liquid-like state. It is a challenge to determine the point at which the assemblies jam, since both jamming and vitrification lead to a solid-like behavior of the assemblies. Herein, we show a real-time fluorescence imaging method to probe the evolution of the interfacial dynamics of NP surfactants at the water/oil interface using aggregation-induced emission (AIE) as a reporter for the transition of the assemblies into the jammed state. The AIEgens show typical fluorescence behavior at densities at which they can move and rotate. However, when aggregation of these fluorophores occurs, the smaller intermolecular separation distance arrests rotation, and a significant enhancement in the fluorescence intensity occurs.

The strong electrostatic interactions at the oil-water interface between a small molecule, 5,10,15,20-tetrakis(4-sulfonatophenyl)porphyrin, H₆ TPPS, dissolved in water, and an amine terminated hydrophobic polymer dissolved in oil are shown to produce a supramolecular polymer surfactant (SPS) of H₆ TPPS at the interface with a binding energy that is sufficiently strong to allow an intermolecular aggregation of the supramolecular polymers. SPSs at the oil-water interface are confirmed by in situ real-space atomic force microcopy imaging. The assemblies of these aggregates can jam at the interface, opening a novel route to kinetically trap the liquids in non-equilibrium shapes. The elastic film, comprised of SPSs, wrinkles upon compression, providing a strategy to stabilize liquids in non-equilibrium shapes.