Dislocation networks are one of the most principle sources deteriorating the performances of devices based on lattice-mismatched heteroepitaxial systems. We demonstrate here a technique enabling fully coherent germanium (Ge) islands selectively grown on nanotip-patterned Si(001) substrates. The silicon (Si)-tip-patterned substrate, fabricated by complementary metal oxide semiconductor compatible nanotechnology, features ∼50-nm-wide Si areas emerging from a SiO2 matrix and arranged in an ordered lattice. Molecular beam epitaxy growths result in Ge nanoislands with high selectivity and having homogeneous shape and size. The ∼850 °C growth temperature required for ensuring selective growth has been shown to lead to the formation of Ge islands of high crystalline quality without extensive Si intermixing (with 91 atom % Ge). Nanotip-patterned wafers result in geometric, kinetic-diffusion-barrier intermixing hindrance, confining the major intermixing to the pedestal region of Ge islands, where kinetic diffusion barriers are, however, high. Theoretical calculations suggest that the thin Si/Ge layer at the interface plays, nevertheless, a significant role in realizing our fully coherent Ge nanoislands free from extended defects especially dislocations. Single-layer graphene/Ge/Si-tip Schottky junctions were fabricated, and thanks to the absence of extended defects in Ge islands, they demonstrate high-performance photodetection characteristics with responsivity of ∼45 mA W(-1) and an Ion/Ioff ratio of ∼10(3).

Advanced semiconductor heterostructures are at the very heart of many modern technologies, including aggressively scaled complementary metal oxide semiconductor transistors for high performance computing and laser diodes for low power solid state lighting applications. The control of structural and compositional homogeneity of these semiconductor heterostructures is the key to success to further develop these state-of-the-art technologies. In this article, we report on the lateral distribution of tilt, composition, and strain across step-graded SiGe strain relaxed buffer layers on 300 mm Si(001) wafers treated with and without chemical-mechanical polishing. By using the advanced synchrotron based scanning X-ray diffraction microscopy technique K-Map together with micro-Raman spectroscopy and Atomic Force Microscopy, we are able to establish a partial correlation between real space morphology and structural properties of the sample resolved at the micrometer scale. In particular, we demonstrate that the lattice plane bending of the commonly observed cross-hatch pattern is caused by dislocations. Our results show a strong local correlation between the strain field and composition distribution, indicating that the adatom surface diffusion during growth is driven by strain field fluctuations induced by the underlying dislocation network. Finally, it is revealed that a superficial chemical-mechanical polishing of cross-hatched surfaces does not lead to any significant change of tilt, composition, and strain variation compared to that of as-grown samples.