The realization of high performance Ni-rich layered cathodes remains a challenge because of the multiple degradation factors that concurrently operate during battery cycling. In particular, depletion of oxygen charge and consequent lattice-oxygen instability at deep charge state accelerate the subsequent chemomechanical degradation mechanisms. Among the proposed methodologies, doping has proven to be effective in enhancing the cathode cycle life by stabilizing the layered structure. Herein, we achieved the electrochemically stabilized Ni-rich LiNi0.92Co0.04Mn0.04O2 through Zr doping, resulting in a 15% increase of the capacity retention after 100 cycles. In-depth investigations are conducted to unveil the effects of Zr doping on the layered cathode, and in particular, the critical role of Zr doping on the lattice oxygen stability is systematically studied. By combining state-of-the-art magnetometer characterization, X-ray analysis, and first-principles calculation, we reveal that Zr doping positively contributes the to lattice oxygen stability by alleviating the oxygen charge loss at deep charge, thereby improving the cathode electrochemical reversibility. Our findings provide an insight into the Zr doping mechanism and help to design Ni-rich layered oxides for future applications.

Despite the high energy density of lithium-rich layered-oxide electrodes, their real-world implementation in batteries is hindered by the substantial voltage decay on cycling. This voltage decay is widely accepted to mainly originate from progressive structural rearrangements involving irreversible transition-metal migration. As prevention of this spontaneous cation migration has proven difficult, a paradigm shift toward management of its reversibility is needed. Herein, we demonstrate that the reversibility of the cation migration of lithium-rich nickel manganese oxides can be remarkably improved by altering the oxygen stacking sequences in the layered structure and thereby dramatically reducing the voltage decay. The preeminent intra-cycle reversibility of the cation migration is experimentally visualized, and first-principles calculations reveal that an O2-type structure restricts the movements of transition metals within the Li layer, which effectively streamlines the returning migration path of the transition metals. Furthermore, we propose that the enhanced reversibility mitigates the asymmetry of the anionic redox in conventional lithium-rich electrodes, promoting the high-potential anionic reduction, thereby reducing the subsequent voltage hysteresis. Our findings demonstrate that regulating the reversibility of the cation migration is a practical strategy to reduce voltage decay and hysteresis in lithium-rich layered materials.