In BaTiO3 single crystals, we observed a strain-driven phase transition from the tetragonal phase to the tetragonal-orthorhombic phase boundary which can be introduced by slow cycling compressions (a loading of up to 0.5 GPa, strain rate of 10-4 s-1, and 100 cycles) at room temperature. Different from the well-known tetragonal to cubic phase transition under stress (∼2 GPa), it only takes place locally around bent 90° domain walls. The inhomogeneous local stress and electrical fields as well as the mobile point defect pinning effect contribute to the phase re-entrance. Through comparison experiments by in situ synchrotron x-ray diffraction, Raman scattering, and (scanning) transmission electron microscopy, we explored the phase transition mechanism. Based on that, we developed a mechanical method to obtain well-stabilized high-density thermotropic phase boundary structures (with tetragonal, orthorhombic, and bridging monoclinic phases) in BaTiO3 for potential applications.

Large superelastic deformation in ferroelastic-ferroelectrics (FMs) is a complex phenomenon involving multiple mechanisms operating simultaneously. Understanding how these mechanisms contribute corporately is critical to apply this useful property to the intrinsically brittle FMs, which can therefore display both excellent functional and mechanical performance. Here, we have directly observed and quantitatively analyzed in situ in a transmission electron microscope the three main mechanisms of twinning domain, phase transformation and mobile point defect contributing to extremely large superelastic deformation in single-crystal BaTiO3 (5.0% strain) and Pb(Mg1/3Nb2/3)O3-PbTiO3 (10.1% strain). Our results reveal the hierarchical origin of large recoverable strain in “brittle” FMs.

The Hall-Petch relationship, according to which the strength of a metal increases as the grain size decreases, has been reported to break down at a critical grain size of around 10 to 15 nanometres^1,2. As the grain size decreases beyond this point, the dominant mechanism of deformation switches from a dislocation-mediated process to grain boundary sliding, leading to material softening. In one previous approach, stabilization of grain boundaries through relaxation and molybdenum segregation was used to prevent this softening effect in nickel-molybdenum alloys with grain sizes below 10 nanometres³. Here we track in situ the yield stress and deformation texturing of pure nickel samples of various average grain sizes using a diamond anvil cell coupled with radial X-ray diffraction. Our high-pressure experiments reveal continuous strengthening in samples with grain sizes from 200 nanometres down to 3 nanometres, with the strengthening enhanced (rather than reduced) at grain sizes smaller than 20 nanometres. We achieve a yield strength of approximately 4.2 gigapascals in our 3-nanometre-grain-size samples, ten times stronger than that of a commercial nickel material. A maximum flow stress of 10.2 gigapascals is obtained in nickel of grain size 3 nanometres for the pressure range studied here. We see similar patterns of compression strengthening in gold and palladium samples down to the smallest grain sizes. Simulations and transmission electron microscopy reveal that the high strength observed in nickel of grain size 3 nanometres is caused by the superposition of strengthening mechanisms: both partial and full dislocation hardening plus suppression of grain boundary plasticity. These insights contribute to the ongoing search for ultrastrong metals via materials engineering.

The operating conditions of functional materials usually involve varying stress fields, resulting in structural changes, whether intentional or undesirable. Complex multiscale microstructures including defects, domains, and new phases, can be induced by mechanical loading in functional materials, providing fundamental insight into the deformation process of the involved materials. On the other hand, these microstructures, if induced in a controllable fashion, can be used to tune the functional properties or to enhance certain performance. In situ nanomechanical tests conducted in scanning/transmission electron microscopes (STEM/TEM) provide a critical tool for understanding the microstructural evolution in functional materials. Here, select results on a variety of functional material systems in the field are presented, with a brief introduction into some newly developed multichannel experimental capabilities to demonstrate the impact of these techniques.