The Second International Workshop on Ambient Pressure X-ray Photoelectron Spectroscopy (APXPS) was held at Lawrence Berkeley National Laboratory (LBNL) in Berkeley, CA, from December 7–9, 2015. It brought together more than 100 participants from 17 countries. The workshop followed the inaugural meeting at the French synchrotron SOLEIL in December 2014, which was organized by François Rochet. The strong interest in these workshops reflects the growth of the APXPS community over the last decade, with instruments now operational at more than 12 synchrotrons around the world (see SRN, Vol. 27, No. 2, pp. 14–23 (2014)), and a steady increase in the number of laboratory instruments. APXPS has established itself as an important method for the investigation of surfaces and interfaces under in situ and operando conditions, including liquid/vapor and liquid/solid interfaces.

Ambient-pressure X-ray photoelectron spectroscopy (APXPS) has contributed greatly to a wide range of research fields, including environmental science [1], catalysis [2], and electrochemistry [3], to name a few. The use of this technique at synchrotron facilities primarily focused on probing the solid/gas interface; however, it quickly advanced to the probing of liquid/vapor interfaces [4, 5] and solid/liquid interfaces through an X-ray-transparent window [6–8]. Most recently, combining APXPS with “Tender” X-rays (~2.5 keV to 8 keV) on beamline 9.3.1 at the Advanced Light Source in Lawrence Berkeley National Laboratory (which can generate photoelectrons with much longer inelastic mean free paths) has enabled us to probe the solid/liquid interface without needing a window [9]. This innovation allows us to probe interfacial chemistries of electrochemically controlled solid/liquid interfaces undergoing charge transfer reactions [9]. These advancements have transitioned APXPS from a traditional surface science tool to an essential interface science technique.

The need to reduce atmospheric CO₂ concentrations necessitates CO₂ capture technologies for conversion into stable products or long-term storage. A single pot solution that simultaneously captures and converts CO₂ could minimize additional costs and energy demands associated with CO₂ transport, compression, and transient storage. While a variety of reduction products exist, currently, only conversion to C₂₊ products including ethanol and ethylene are economically advantageous. Cu-based catalysts have the best-known performance for CO₂ electroreduction to C₂₊ products. Metal Organic Frameworks (MOFs) are touted for their carbon capture capacity. Thus, integrated Cu-based MOFs could be an ideal candidate for the one-pot capture and conversion. In this paper, we review Cu-based MOFs and MOF derivatives that have been used to synthesize C₂₊ products with the objective of understanding the mechanisms that enable synergistic capture and conversion. Furthermore, we discuss strategies based on the mechanistic insights that can be used to further enhance production. Finally, we discuss some of the challenges hindering widespread use of Cu-based MOFs and MOF derivatives along with possible solutions to overcome the challenges.

Nickel-based catalysts play an important role in the chemical transformation of CO2. A fundamental understanding of the interaction between CO2 and Ni surfaces at atomic level is necessary. In this study, the interfacial reactions of CO2 and CO2 + H2O mixture on Ni(111) as well Ni(100) surfaces were investigated using ambient pressure X-ray photoelectron spectroscopy as well as theoretical calculations. The results indicate that the distributions of dissociation products are very different on the Ni(111) and Ni(100) surfaces. Carbonate, CO, and graphitic carbon formed on both Ni(111) and Ni(100) surfaces in the presence of 0.2 Torr CO2. However, more than 90% adsorption species on the Ni(111) surface is the carbonate, whereas the Ni(100) surface is mainly covered by adsorbed CO∗ and graphitic carbon. The co-adsorption of H2O weakens the influence of structure effect on the interfacial interaction between CO2 and Ni surfaces. Furthermore, the density functional theory calculations suggest that the activation of CO2 on Ni(111) and Ni(100) tends to follow different reaction paths, which are consistent with the experimental results.

The interaction of water with metal surfaces is at the heart of electrocatalysis. But there remain enormous uncertainties about the atomistic interactions at the electrode-electrolyte interface (EEI). As the first step toward an understanding of the EEI, we report here the details of the initial steps of H₂O adsorption and complex formation on a Ag(111) surface, based on coupling quantum mechanics (QM) and ambient-pressure X-ray photoelectron spectroscopy (APXPS) experiments. We find a close and direct comparison between simulation and experiment, validated under various isotherm and isobar conditions. We identify five observable oxygen-containing species whose concentrations depend sensitively on temperature and pressure: chemisorbed O* and OH*, H₂O* stabilized by hydrogen bond interactions with OH* or O*, and multilayer H₂O*. We identify the species experimentally by their O 1s core-level shift that we calculate with QM along with the structures and free energies as a function of temperature and pressure. This leads to a chemical reaction network (CRN) that we use to predict the time evolution of their concentrations over a wide range of temperature (298-798 K) and pressure conditions (10^-6-1 Torr), which agree well with the populations determined from APXPS. This multistep simulation CRN protocol should be useful for other heterogeneous catalytic systems.

Achieving a molecular-level understanding of interfacial (photo)electrochemical processes is essential in order to tailor novel and highly-performing catalytic systems. The corresponding recent development of in situ and operando tools has posed new challenges on experimental architectures. In this study, we use ambient pressure X-ray photoelectron spectroscopy (AP-XPS) to probe the solid/liquid electrified interface of a polycrystalline Pt sample in contact with an alkaline electrolyte during hydrogen and oxygen evolution reactions. Using the “dip-and-pull” technique to probe the interface through a thin liquid layer generated on the sample surface, we observe that the electrolyte meniscus becomes unstable under sustained driving of an electrolyte-consuming reaction (such as water oxidation). The addition of an electrochemically inert supporting electrolyte mitigates this issue, maintaining a stable meniscus layer for prolonged reaction times. In contrast, for processes in which the electrolyte is replenished in the reaction pathway (i.e. water reduction in alkaline conditions), we find that the solid/liquid interface remains stable without addition of a secondary supporting electrolyte. The approach described in this work allows the extension of operando AP-XPS capabilities using the “dip-and-pull” method to a broader class of reactions consuming ionic species during complex interfacial faradaic processes.

Hydrogen spillover is a catalytic process that occurs by surface reaction and subsequent diffusion to reversibly provide a massive amount of hydrogen dopants in correlated oxides, but the mechanism at the surface of correlated oxides with metal catalyst are not well understood. Here we show that a significant amount of oxygen is released from the surface of correlated VO₂ films during hydrogen spillover, contrary to the well-established observation of the formation of hydrogen interstitials in the bulk part of VO₂ films. By using ambient-pressure X-ray photoelectron spectroscopy, we prove that the formation of surface oxygen vacancies is a consequence of a favorable reaction for the generation of weakly adsorbed H₂O from surface O atoms that have low coordination and weak binding strength. Our results reveal the importance of in situ characterization to prove the dynamic change during redox reaction and present an opportunity to control intrinsic defects at the surface.

Using ambient pressure XPS (APXPS), we explored carbon dioxide (CO2) adsorption and CO2 hydrogenation on Pt(1 1 1) single crystal surface to observe the activation of CO2 and the subsequent reaction mechanism. In pure CO2, we observed CO adsorbates and adsorbed oxygen on Pt(1 1 1) derived from CO2 dissociation at room temperature. The introduction of H2 (at a pressure ratio of 1:1 (H2:CO2)) increased the production of CO across all temperatures by facilitating the removal of surface oxygen. As a consequence, the surface could expose sites that could then be utilized for producing CO. Under these conditions, the reverse water–gas shift (RWGS) reaction was observed starting at 300 oC. At higher H2 partial pressure (10:1 (H2:CO2)), the RWGS reaction initiated at a lower temperature of 200 oC and continued to enhance the conversion of CO2 with increasing temperatures. Our results revealed that CO2 was activated on a clean Pt(1 1 1) surface through the dissociation mechanism to form adsorbed CO and O at room temperature and at elevated temperatures. Introducing H2 facilitated the RWGS as adsorbed oxygen was consumed continuously to form H2O, and adsorbed CO desorbed from the surface at elevated temperatures. This work clearly provides direct experimental evidence for the surface chemistry of CO2 dissociation and demonstrates how hydrogen impacts the RWGS reaction on a platinum surface.

A national priority is to convert CO₂ into high-value chemical products such as liquid fuels. Because current electrocatalysts are not adequate, we aim to discover new catalysts by obtaining a detailed understanding of the initial steps of CO₂ electroreduction on copper surfaces, the best current catalysts. Using ambient pressure X-ray photoelectron spectroscopy interpreted with quantum mechanical prediction of the structures and free energies, we show that the presence of a thin suboxide structure below the copper surface is essential to bind the CO₂ in the physisorbed configuration at 298 K, and we show that this suboxide is essential for converting to the chemisorbed CO₂ in the presence of water as the first step toward CO₂ reduction products such as formate and CO. This optimum suboxide leads to both neutral and charged Cu surface sites, providing fresh insights into how to design improved carbon dioxide reduction catalysts.

Ambient pressure XPS has demonstrated its great potential in probing the solid/liquid interface, which is a central piece in electrocatalytic, corrosion, and energy storage systems. Despite the advantage of ambient pressure XPS being a surface sensitive characterization technique, the ability of differentiating the surface adsorbed species (∼Å scale) and bulk electrolyte (∼10 nm scale) in the spectrum depends on the delicate balance between bulk solution concentration (C), surface coverage (θ), bulk liquid layer thickness (L), and inelastic mean free path (λ) as a function of photon energy. By investigating a model system of gold dissolving in a bromide solution, the connection between theoretical prediction at the atomic resolution and macroscopic observable spectrum is established.